聚苯氧基磷酸联苯二酚酯/聚磷酸铵膨胀阻燃剂对环氧树脂阻燃性能影响研究

来方; 付海; 赵欧; 张永航; 李霈; 陈仕梅; 顾锡军; 班大明

doi:10.11777/j.issn1000-3304.2017.16156

您当前的位置：

首页 >

文章列表页 >

聚苯氧基磷酸联苯二酚酯/聚磷酸铵膨胀阻燃剂对环氧树脂阻燃性能影响研究

研究论文 | 更新时间：2021-05-18

- 聚苯氧基磷酸联苯二酚酯/聚磷酸铵膨胀阻燃剂对环氧树脂阻燃性能影响研究
- Influence of Poly (biphenyl phenoxy phosphate)/APP on Flame Retardancy of Epoxy Resin
- 高分子学报 2017年第4期页码：692-699
- 作者机构：
  
  贵州师范大学化学与材料科学学院贵阳 550001
- 作者简介：
  
  班大明, E-mail: bdaming@gznu.edu.cn Da-ming Ban, E-mail: bdaming@gznu.edu.cn
- 基金信息：
  
  国家自然科学基金(51273049);贵州省科技创新人才团队(黔科合人才团队[2014]4006号);贵州省科技厅社发攻关项目(黔科合SY字[2013]3146号)
- DOI：10.11777/j.issn1000-3304.2017.16156
  中图分类号：
- 纸质出版日期：2017-4-20，
  
  收稿日期：2016-4-29，
  
  修回日期：2016-7-5，
扫描看全文
来方, 付海, 赵欧, 张永航, 李霈, 陈仕梅, 顾锡军, 班大明. 聚苯氧基磷酸联苯二酚酯/聚磷酸铵膨胀阻燃剂对环氧树脂阻燃性能影响研究[J]. 高分子学报, 2017,(4):692-699.

Fang Lai, Hai Fu, Ou Zhao, Yong-hang Zhang, Pei Li, Shi-mei Chen, Xi-jun Gu, Da-ming Ban. Influence of Poly (biphenyl phenoxy phosphate)/APP on Flame Retardancy of Epoxy Resin[J]. Acta Polymerica Sinica, 2017,(4):692-699.
来方, 付海, 赵欧, 张永航, 李霈, 陈仕梅, 顾锡军, 班大明. 聚苯氧基磷酸联苯二酚酯/聚磷酸铵膨胀阻燃剂对环氧树脂阻燃性能影响研究[J]. 高分子学报, 2017,(4):692-699. DOI： 10.11777/j.issn1000-3304.2017.16156.

Fang Lai, Hai Fu, Ou Zhao, Yong-hang Zhang, Pei Li, Shi-mei Chen, Xi-jun Gu, Da-ming Ban. Influence of Poly (biphenyl phenoxy phosphate)/APP on Flame Retardancy of Epoxy Resin[J]. Acta Polymerica Sinica, 2017,(4):692-699. DOI： 10.11777/j.issn1000-3304.2017.16156.

摘要

以聚苯氧基磷酸联苯二酚酯（PBPP）与聚磷酸铵（APP）组成复合阻燃剂，对环氧树脂（EP）进行阻燃改性.通过氧指数（LOI）、垂直燃烧（UL-94）、热失重（TGA）、锥形量热（CONE）和扫描电镜（SEM）等方法研究改性环氧树脂的阻燃性能和阻燃机理.结果表明，PBPP/APP体系对EP具有较好的阻燃性能，阻燃剂添加量为10%时能使环氧树脂的氧指数提高到29.6%，垂直燃烧等级达到UL94 V-0级，残炭量大大增加；平均热释放速率下降45.7%，热释放速率峰值下降51.0%，有效燃烧热平均值下降21.1%；TGA、CONE、SEM等综合分析显示了PBPP/APP改性后的环氧树脂比纯环氧树脂具有更高的热稳定性，燃烧后能够形成连续、致密、封闭、坚硬的焦化炭层，在聚合物表面产生有效覆盖、隔绝了氧气，改善了环氧树脂的燃烧性能.

Abstract

A novel and efficient flame retardant additive poly (biphenyl phenoxy phosphate) (PBPP) was prepared by reaction of biphenol with dichloro phenoxyphosphate. The structure of PBPP was confirmed by Fourier transform infrared spectroscopy (FTIR). Thermogravimetric analysis (TGA) result demonstrated that the initial decomposition temperature of PBPP was 253 ℃

with a char residue of 51.41 wt% at 700 ℃. PBPP blended with ammonium polyphosphate (APP) at the ratio of 1:2 was incorporated into epoxy resins and cured by

-phenylenediamine (

-PDA) to form a flame retardant thermoset (FR-EP). The effect of intumescent flame retardant (IFR) composed of PBPP and APP on epoxy resin was investigated by limiting oxygen index (LOI)

vertical burning (UL-94)

TGA

cone calorimetry (CONE) and scanning electron microscope (SEM). Comparing epoxy resin retardant common used with 30 wt% of APP

this PBPP based flame retardant with PBPP amount of 10 wt% showed similar retardant effect as the classical one. At this low addition amount of PBPP

this PBPP/APP modified FR-EP past UL-94 V0 grade and gave 29.6% as the LOI value at the same time. TGA test results revealed that the incorporation of PBPP/APP into epoxy resins stimulated the degradation of thermosets at initial degradation stage and charring formation. The char yield of the FR-EP thermosets increased from 15.02 wt% to 22.17 wt% at 700 ℃. According to the cone test

heat release rate (HRR)

total heat release (THR) and total smoke release (TSR) were all decreased dramatically in the FR-EP. The cone test showed that the av-HRR

pk-HRR

and av-EHC of the FR-EP were lowered by 45.7%

51.0% and 21.1%

respectively

in comparison with those of the pure EP. The char residue of the new FR-EP was about 80 times of that observed in the pure EP. Moreover

PBPP/APP promoted the epoxy resins thermosets forming more homogeneous and compact char layer during combustion as seen by SEM. Char layer prevented the inner matrix from further decomposition and combustion

which enhanced by consequence the flame retardancy of the FR-EP thermosets. The tensile strength of EP was also affect by loading of the flame retardant with a decrease at lower loading and an increased at higher loading.

关键词

聚苯氧基磷酸联苯二酚酯聚磷酸铵环氧树脂膨胀型阻燃剂协同作用

Keywords

Poly (biphenyl phenoxy phosphate)Ammonium polyphosphateEpoxy resinIntumescent flame retardantSynergistic

references

M Drehe , V Simulescu , G Ilia . Rev Chem Eng , 2008 . 24 263 - 302.

S V Levchik , E D Weil . J Fire Sci , 2006 . 24 345 - 364 . DOI:10.1177/0734904106068426http://doi.org/10.1177/0734904106068426.

L Chen , Y Z Wang . Polym Adv Technol , 2010 . 21 1 - 26 . DOI:10.1016/j.apt.2009.12.012http://doi.org/10.1016/j.apt.2009.12.012.

E D Weil , S V Levchik . J Fire Sci , 2004 . 22 293 - 303 . DOI:10.1177/0734904104041210http://doi.org/10.1177/0734904104041210.

Y Shi , G J Wang . Prog Org Coat , 2016 . 97 1 - 9 . DOI:10.1016/j.porgcoat.2016.02.023http://doi.org/10.1016/j.porgcoat.2016.02.023.

W Zhao , J P Liu , H Peng , J Y Liao , X J Wang . Polym Degrad Stab , 2015 . 118 120 - 129 . DOI:10.1016/j.polymdegradstab.2015.04.023http://doi.org/10.1016/j.polymdegradstab.2015.04.023.

B Liang , G Wang , X Hong , J Long , N Tsubaki . High Perform Polym , 2016 . 28 110 - 118 . DOI:10.1177/0954008315604036http://doi.org/10.1177/0954008315604036.

G Camino , L Costa , L Trossarelli , F Costanzi , G Landoni . Polym Degrad Stab , 1984 . ( 4 ): 243 - 252.

G Camino , L Costa , L Trossarelli . Polym Degrad Stab , 1984 . 7 25 DOI:10.1016/0141-3910(84)90027-2http://doi.org/10.1016/0141-3910(84)90027-2.

G Camino , L Costa , L Trossarelli . Polym Degrad Stab , 1985 . ( 3 ): 203 - 211.

H Horacek , S Pieh . Polym Inter , 2000 . 49 1106 DOI:10.1002/(ISSN)1097-0126http://doi.org/10.1002/(ISSN)1097-0126.

Ban Daming (班大明), Qin Haoli (秦好丽), Zhao Ou (赵欧), Zhang Yonghang (张永航), Liu Zhenmei (刘真美), Wei Wanli (韦万丽), CN Patent, CN102786694A. 2012-09-07

X B Lin , S L Du , J W Long , L Chen , Y Z Wang . ACS Appl Mater Inter , 2016 . 8 881 - 890 . DOI:10.1021/acsami.5b10287http://doi.org/10.1021/acsami.5b10287.

X Wang , Y Hu , S Y Xuan , W Y Xing , Z M Bai , H D Lu . Ind Eng Chem Res , 2011 . 50 713 - 720 . DOI:10.1021/ie1017157http://doi.org/10.1021/ie1017157.

Zhenjie Wei , Weiqu Liu , Hongjing Li , Songqi Ma , Zhenlong Yan . Acta Polymerica Sinica , 2012 . ( 2 ): 148 - 153 . http://www.gfzxb.org/CN/abstract/abstract13561.shtml.

魏振杰 , 刘伟区 , 李宏静 , 马松琪 , 闫振龙 . 高分子学报 , 2012 . ( 2 ): 148 - 153 . http://www.gfzxb.org/CN/abstract/abstract13561.shtml.

Bin Li , Jianqi Wang . Polymer Materials Science and Engineering , 1998 . ( 5 ): 15 - 19.

李斌 , 王建祺 . 高分子材料科学与工程 , 1998 . ( 5 ): 15 - 19.

R C Xie , B J Qu . J Appl Polym Sci , 2001 . 80 1190 - 1197 . DOI:10.1002/(ISSN)1097-4628http://doi.org/10.1002/(ISSN)1097-4628.

S Bourezigot , M Le Bras , R Delobel . Fire Sci , 1995 . 13 3 - 20 . DOI:10.1177/073490419501300101http://doi.org/10.1177/073490419501300101.

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

碳材料表面特性及形貌对阻燃环氧树脂燃烧和热解行为的影响

竹基多孔碳材料的制备及其协同阻燃环氧树脂研究

具有可控降解与抗菌功能的生物基环氧树脂合成

磷化淀粉的合成及其与聚磷酸铵协效阻燃聚乳酸的性能研究