- 对苯乙烯磺酸钠改性炭黑对天然橡胶胶乳力学性能的影响
- EFFECT OF POLY(SODIUM 4-STYRENESULFONAE) MODIFIED CARBON BLACK ON MECHANICAL PROPERTIES OF NATURAL RUBBER LATEX
- 高分子学报 2009年第11期页码：1101-1106
- 作者机构：
- 作者简介：
- 基金信息：
- DOI：10.3724/SP.J.1105.2009.01101
  中图分类号：
- 纸质出版日期：2009-11-20，
扫描看全文
何雪莲, 韩晶杰, 许海燕, 吴驰飞. 对苯乙烯磺酸钠改性炭黑对天然橡胶胶乳力学性能的影响[J]. 高分子学报, 2009,(11):1101-1106.

HE Xuelian, HAN Jingjie, XU Haiyan, WU Chifei. EFFECT OF POLY(SODIUM 4-STYRENESULFONAE) MODIFIED CARBON BLACK ON MECHANICAL PROPERTIES OF NATURAL RUBBER LATEX[J]. Acta Polymerica Sinica, 2009,(11):1101-1106.
何雪莲, 韩晶杰, 许海燕, 吴驰飞. 对苯乙烯磺酸钠改性炭黑对天然橡胶胶乳力学性能的影响[J]. 高分子学报, 2009,(11):1101-1106. DOI： 10.3724/SP.J.1105.2009.01101.

HE Xuelian, HAN Jingjie, XU Haiyan, WU Chifei. EFFECT OF POLY(SODIUM 4-STYRENESULFONAE) MODIFIED CARBON BLACK ON MECHANICAL PROPERTIES OF NATURAL RUBBER LATEX[J]. Acta Polymerica Sinica, 2009,(11):1101-1106. DOI： 10.3724/SP.J.1105.2009.01101.

摘要

在Haake转矩流变仪的热机械作用下，用对苯乙烯磺酸钠（NASS）对炭黑进行预处理，制备了在水介质中具有优异的分散稳定性的亲水性纳米炭黑粒子（PNASS-CB），并将其直接用于天然橡胶胶乳的补强研究.1HNMR和FT-IR结果表明NASS在炭黑表面成功聚合包覆，用热重分析方法计算其包覆率为8.1 wt%，接枝率为2.5 wt%.亲水性炭黑的表面自由能降低，同时，Payne效应和结合胶含量表明亲水性炭黑粒子与橡胶的相互作用强于亲水性炭黑粒子之间的相互作用.因此，亲水性炭黑/天然橡胶胶乳复合材料的硫化时间变短，转化速度加快，硫化胶的撕裂强度提高了85%，拉伸强度提高了30%，断裂伸长率提高了20%.

Abstract

A novel strategy of radical polymerization of sodium 4-styrenesulfonate (NASS) on the surface of carbon black (CB) in solid state is developed to prepare water-dispersible carbon nanoparticles (PNASS-CB).A high performance of natural rubber latex (NRL)/PNASS-CB composite is gained by latex compounding technique.Proton nuclear magnetic resonance (1H-NMR) results show the presence of PNASS chains on the surface of CB

and the encapsulating ratio is 8.1 wt% and grafting ratio is 2.5 wt% by TGA.The surface energy of PNASS-CB was decreased

the interaction between carbon black was weakened

and the carbon-rubber interaction was enhanced.And the carbon nanoparticles are uniformly dispersed in the composite as the result of RPA.When compared to the NRL/pristine CB composite

the tear strength

tensile strength and elongation at break of the obtained composite are increased by 85%

30% and 20%

respectively.

关键词

热机械作用对乙烯苯磺酸钠天然橡胶胶乳硫化性能力学性能

Keywords

references

更多指标>

浏览量

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

高强度两性离子聚合物防污减阻水凝胶涂层的制备

聚丁二酸丁二酯/纳米高岭土共混体系结晶及力学性能研究

酮肼交联及硅烷偶联水性聚氨酯的成膜机理及其性能研究

聚对苯二甲酰对苯二胺纤维的热老化行为与机理研究

SMA/蒙脱石纳米复合材料增容PA6/ABS共混体系